Plastcom SLOVAMID 66 BT TS PA66, basic type, thermal stabilityNylon 66, Heat StabilizedPlastcom spol. s r.o.產(chǎn)品說明：FeaturesModified for general use, with excellent manufacturing properties, characterized by high strength and toughness also at minus temperatures. Used in automotive, electrical, engineering and consumer goods industry. Application: electric tools, gear wheels, clamps, fasteners, toolbodies, webbing slings for cable harnesses.Packaging, transport, stockingThe product is packed in hermetically closed thick-walled 25 kg PE bags, on a 1.000 kg palette coated in a stretch foil, in big bags with a thick PE foil fixed on a 1.000 kg palette, in paper octabins with a thick PE foil fixed on a 1.000 kg palette or in other packaging according to customer re The transport is provided in closed-up vehicles where the material is protected against movement and mechanical damage. The product requires stocking in closed-up, dry places protected against sun and thermal radiation.Information Provided by Plastcom spol. s r.o.物性信息：物理性能額定值 (公制)額定值 (英制)測試方法密度1.13 g/cc0.0408 lb/in3粘度測量1.8 - 1.931.8 - 1.93線性成型收縮率0.018 cm/cm0.018 in/in線性成型收縮率，橫向0.0193 cm/cm0.0193 in/in熔體流動(dòng)速率4.0 g/10 min@Load 0.325 kg, Temperature 270 °C4.0 g/10 min@Load 0.716 lb, Temperature 518 °F機(jī)械性能額定值 (公制)額定值 (英制)測試方法抗張強(qiáng)度(斷裂)80.0 MPa11600 psi伸長率 (斷裂)3.0 %3.0 %拉伸模量3.20 GPa464 ksi彎曲強(qiáng)度100 MPa14500 psi彎曲模量2.70 GPa392 ksi簡支梁無缺口沖擊強(qiáng)度NB@Temperature 23.0 °CNB@Temperature 73.4 °FNB@Temperature -20.0 °CNB@Temperature -4.00 °F簡支梁缺口沖擊強(qiáng)度0.200 J/cm2@Temperature -20.0 °C0.952 ft-lb/in2@Temperature -4.00 °F0.500 J/cm2@Temperature 23.0 °C2.38 ft-lb/in2@Temperature 73.4 °F電氣性能額定值 (公制)額定值 (英制)測試方法體積電阻率1.00e+12 ohm-cm1.00e+12 ohm-cm表面電阻1.00e+14 ohm1.00e+14 ohm介電強(qiáng)度30.0 kV/mm762 kV/in相比耐漏電起痕指數(shù)(CTI)600 V600 V熱性能額定值 (公制)額定值 (英制)測試方法熔融溫度260 °C500 °F載荷下熱變形溫度(1.8 MPa)68.0 °C154 °F維卡軟化溫度250 °C482 °FB可燃性(UL94)HBHB灼熱絲試驗(yàn)960 °C1760 °F加工性能額定值 (公制)額定值 (英制)測試方法加工（熔體）溫度°C°F模具溫度80.0 - 90.0 °C°F干燥溫度80.0 °C176 °F干燥時(shí)間4 hour4 hour水分含量0.15 %0.15 %注射壓力70.0 - 120 MPa psi